Combined Hardness Tester NOVOTEST T-UD2

Combined Hardness Tester NOVOTEST T-UD2

Order Catalog


Combined Hardness Tester NOVOTEST T-UD2 is designed for rapid non-destructive hardness testing of :
metals and alloys on standardized hardness scales;
metals with different properties from steel (for example, non-ferrous metals, alloys, cast iron, etc.) with additional scales for calibration;
use the scale of tensile strength (Rm) for determining the tensile strength of carbon steel products pearlitic by automatically converting from Brinell (HB) hardness scale.
Device implements 2 methods of testing: rebound (Leeb) and ultrasonic contact impedance (UCI). The combination of both methods allows user to test all range of metal products.

UCI method for the hardness testing
The UCI hardness measuring method complies to ASTM A1038.
The ultrasonic contact impedance (UCI) probe is purposed to be used for hardness measuring in the case of the testing area minimal thickness (from 1 mm), objects of complex surface shape, and for measuring surface hardened layers hardness.
This method is very fast and easy: place the probe on the tested object surface, press the probe with the required effort to the surface and save the hardness value, shown on the display of the device. Small size diamond indenter allows measuring hardness value of all items, which are thicker than 1 mm. The UCI method of hardness testing is the least destructive because the hardness tester NOVOTEST T-UD2 with UCI probe leaves much smaller prints (imprints) than the majority of bench hardness tester would. That’s why a portable hardness tester with UCI probe is the best choice.

Leeb method for the hardness testing
The Leeb hardness measuring method complies to ASTM A956.
The Leeb probe (D type) is used for hardness measuring of massive objects (more than 5 kg, and more than 10 mm) and made of steels non-ferrous metals, cast irons, coarse-grained materials, e.t.c. Also, Leeb method perfectly complements with UCI hardness measuring method when UCI method is not applied.
This method is very fast and easy: place the probe on tested object vertically to the object surface, push the probe to charge the spring, press the button on the top of the probe to make measurement and save the hardness value, shown on the display. For the Leeb measuring method, NOVOTEST-UD2 automatically calculates hardness for a wide range of materials, like steel, stainless steel, cast iron, bronze, aluminum.
The combined hardness tester is the most universal, needs no recalibration, and is fully operational “out of the box”.


UCI probe types 1kgf (10N) 2.2 lbf, 5kgf (50N) 11lbf, 10kgf (98N) 22lbf
Leeb probe types D, DC, DL, C, D+15, E, G
Indenter Diamond indenter (UCI)
Hardened ball (Leeb)
Hardness scale HRC, HB, HV
Measurement hardness range:
Rockwell, HRC
Brinell, HB
Vickers, HV
20 – 70
90 – 450
230 – 940
Measuring accuracy HV+ / – 3%
HRC+ / – 1,5%
HB+ / – 3%
Standards ASTM A1038, ASTM A956, ASTM E140
Measuring direction Any direction 360°
Materials UCI probe – pre-calibrated for steel.
Leeb probe – pre-calibrated for steel, alloy steel, stainless steel, aluminum or cast iron.
Additional custom scales and materials for calibration.
Operating temperature range, ° C -20 … +40
Power supply 2pcs AA batteries
Dimensions, mm 120x60x25
Weight of electronic unit with battery, no more, kg 0.2
Batteries life, not less, h 20